Aluminum (Al)	Al1(l)
T(K)	Cp	S	-[G-H(Tr)]/T	H-H(Tr)	delta-f H	delta-f G	log Kf
0														
100														
200														
250														
298.15	24.209	39.549	39.549	0.	10.562	7.201	-1.262
300	24.247	39.699	39.550	0.045	10.562	7.180	-1.250
350	25.113	43.505	39.848	1.280	10.562	6.617	-0.987
400	25.784	46.904	40.522	2.553	10.562	6.053	-0.790
450	26.335	49.973	41.404	3.856	10.562	5.489	-0.637
500	26.842	52.774	42.403	5.186	10.562	4.926	-0.515
600	27.886	57.759	44.557	7.921	10.562	3.798	-0.331
700	29.100	62.146	46.762	10.769	10.562	2.671	-0.199
720.000	29.371	62.969	47.201	11.353	GLASS <--> LIQUID
720.000	31.751	62.969	47.201	11.353	TRANSITION
800	31.751	66.315	48.948	13.893	10.706	1.535	-0.100
900	31.751	70.054	51.089	17.068	10.740	0.384	-0.022
933.450	31.751	71.213	51.790	18.131	CRYSTAL <--> LIQUID
1000	31.751	73.400	53.156	20.244	0. 0. 0.
1100	31.751	76.426	55.136	23.419	0.	0.	0.
1200	31.751	79.189	57.027	26.594	0.	0.	0.
1300	31.751	81.730	58.831	29.769	0.	0.	0.
1400	31.751	84.083	60.552	32.944	0.	0.	0.
1500	31.751	86.273	62.194	36.119	0.	0.	0.
1600	31.751	88.323	63.764	39.294	0.	0.	0.
1700	31.751	90.247	65.266	42.469	0.	0.	0.
1800	31.751	92.062	66.704	45.644	0.	0.	0.
1900	31.751	93.779	68.085	48.819	0.	0.	0.
2000	31.751	95.408	69.410	51.994	0.	0.	0.
2100	31.751	96.957	70.686	55.169	0.	0.	0.
2200	31.751	98.434	71.914	58.344	0.	0.	0.
2300	31.751	99.845	73.098	61.519	0.	0.	0.
2400	31.751	101.196	74.240	64.694	0.	0.	0.
2500	31.751	102.493	75.345	67.870	0.	0.	0.
2600	31.751	103.738	76.413	71.045	0.	0.	0.
2700	31.751	104.936	77.447	74.220	0.	0.	0.
2790.812	31.751	105.986	78.359	77.103	FUGACITY = 1 bar
2800	31.751	106.091	78.450	77.395	293.901 0.968  0.018
2900	31.751	107.205	79.422	80.570	-292.806	11.479	-0.207
3000	31.751	108.281	80.366	83.745	-291.710	21.953	-0.382