Aluminum Iodide (AlI3)	Al1I3(l)
T(K)	Cp	S	-[G-H(Tr)]/T	H-H(Tr)	delta-f H	delta-f G	log Kf
0														
100														
200														
250														
298.15	121.336	223.648	223.648	0.	-289.444	-295.752	51.815
300	121.336	224.398	223.650	0.224	-289.415	-295.792	51.502
400	121.336	259.305	228.409	12.358	-312.247	-297.280	38.821
464.150	121.336	277.352	233.957	20.142	CRYSTAL <--> LIQUID
500	121.336	286.380	237.397	24.492	375.041  287.541 30.039
600	121.336	308.502	247.460	36.625	-371.274	-270.397	23.540
700	121.336	327.206	257.551	48.759	-367.639	-253.873	18.944
800	121.336	343.408	267.293	60.892	-364.155	-237.860	15.531
900	121.336	357.700	276.559	73.026	-360.848	-222.274	12.900
1000	121.336	370.484	285.324	85.160	-368.333	-206.286	10.775
1100	121.336	382.048	293.600	97.293	-365.097	-190.238	9.034
1200	121.336	392.606	301.417	109.427	-361.887	-174.483	7.595
1300	121.336	402.318	308.810	121.560	-358.713	-158.995	6.389
1400	121.336	411.310	315.814	133.694	-355.585	-143.750	5.363
1500	121.336	419.681	322.463	145.828	-352.517	-128.726	4.483
1600	121.336	427.512	328.786	157.961	-349.524	-113.905	3.719
1700	121.336	434.868	334.812	170.095	-346.619	-99.268	3.050
1800	121.336	441.803	340.565	182.228	-343.812	-84.800	2.461
1900	121.336	448.364	346.068	194.362	-341.109	-70.485	1.938
2000	121.336	454.587	351.339	206.496	-338.511	-56.309	1.471