Nickel Chloride (NiCl2)	Cl2Ni1(l)
T(K)	Cp	S	-[G-H(Tr)]/T	H-H(Tr)	delta-f H	delta-f G	log Kf
0														
100														
200														
298.15	71.659	151.810	151.810	0.	-233.517	-203.362	35.628
300	71.747	152.253	151.811	0.133	-233.495	-203.175	35.376
400	76.289	173.562	154.685	7.551	-232.275	-193.250	25.236
500	78.898	190.896	160.249	15.324	-231.041	-183.638	19.184
600	79.881	205.376	166.597	23.267	-230.007	-174.259	15.171
700	80.313	217.720	173.041	31.275	-228.993	-165.038	12.315
800	80.900	228.476	179.312	39.331	-227.724	-155.989	10.185
880.000	81.773	236.225	184.139	45.836	GLASS <--> LIQUID
880.000	101.186	236.225	184.139	45.836	TRANSITION
900	101.186	238.499	185.322	47.860	-226.045	-147.103	8.538
1000	101.186	249.160	191.182	57.978	-222.853	-138.504	7.235
1100	101.186	258.804	196.898	68.097	-219.741	-130.220	6.184
1200	101.186	267.608	202.429	78.215	-216.714	-122.216	5.320
1300	101.186	275.708	207.758	88.334	-213.778	-114.461	4.599
1304.000	101.186	276.018	207.967	88.739	CRYSTAL <--> LIQUID
1400	101.186	283.206	212.883	98.453	210.936  106.929 3.990
1500	101.186	290.187	217.807	108.571	-208.194	-99.596	3.468
1600	101.186	296.718	222.537	118.690	-205.555	-92.443	3.018
1700	101.186	302.852	227.082	128.808	-203.024	-85.451	2.626
1800	101.186	308.636	231.454	138.927	-217.755	-77.891	2.260