Zirconium Fluoride (ZrF2)	F2Zr1(cr,l)
T(K)	Cp	S	-[G-H(Tr)]/T	H-H(Tr)	delta-f H	delta-f G	log Kf
0														
100														
200														
298.15	65.940	75.312	75.312	0.	-962.320	-912.724	159.905
300	66.024	75.720	75.313	0.122	-962.303	-912.416	158.866
400	69.873	95.253	77.950	6.921	-961.282	-895.937	116.997
500	73.220	111.212	83.054	14.079	-960.115	-879.733	91.905
600	76.149	124.827	88.908	21.551	-958.807	-863.777	75.198
700	78.659	136.761	94.909	29.296	-957.380	-848.050	63.282
800	80.626	147.395	100.817	37.262	-955.874	-832.533	54.359
900	82.425	156.997	106.535	45.416	-954.322	-817.209	47.430
1000	84.015	165.766	112.026	53.741	-952.743	-802.058	41.895
1100	85.270	173.834	117.283	62.206	-951.168	-787.066	37.375
1175.000	86.107	179.486	121.074	68.633	CRYSTAL <--> LIQUID
1175.000	100.416	211.534	121.074	106.289	TRANSITION
1200	100.416	213.648	122.981	108.800	-915.322	-772.800	33.639
1300	100.416	221.685	130.269	118.841	-911.919	-761.061	30.580
1400	100.416	229.127	137.068	128.883	-908.578	-749.583	27.967
1500	100.416	236.055	143.438	138.925	-905.311	-738.340	25.711
1600	100.416	242.536	149.432	148.966	-902.125	-727.313	23.744
1700	100.416	248.623	155.089	159.008	-899.029	-716.483	22.015
1800	100.416	254.363	160.447	169.049	-896.033	-705.832	20.483
1900	100.416	259.792	165.534	179.091	-893.144	-695.344	19.116
2000	100.416	264.943	170.376	189.133	-890.371	-685.006	17.891
2100	100.416	269.842	174.997	199.174	-887.719	-674.803	16.785
2200	100.416	274.513	179.415	209.216	-906.521	-663.979	15.765
2300	100.416	278.977	183.648	219.257	-904.551	-652.998	14.830
2400	100.416	283.251	187.709	229.299	-902.577	-642.103	13.975
2500	100.416	287.350	191.614	239.341	-900.594	-631.291	13.190
2600	100.416	291.288	195.372	249.382	-898.599	-620.558	12.467
2700	100.416	295.078	198.995	259.424	-896.587	-609.902	11.799
2800	100.416	298.730	202.492	269.465	-894.557	-599.321	11.180
2900	100.416	302.254	205.872	279.507	-892.505	-588.813	10.606
3000	100.416	305.658	209.142	289.549	-890.429	-578.377	10.070