Iron Iodide (FeI2)	Fe1I2(l)
T(K)	Cp	S	-[G-H(Tr)]/T	H-H(Tr)	delta-f H	delta-f G	log Kf
0														
100														
200														
298.15	112.968	195.430	195.430	0.	-71.046	-86.540	15.161
300	112.968	196.129	195.433	0.209	-70.984	-86.636	15.085
400	112.968	228.628	199.864	11.506	-83.953	-91.771	11.984
500	112.968	253.836	208.231	22.803	-123.705	-89.975	9.400
600	112.968	274.433	217.600	34.099	-119.249	-83.652	7.283
700	112.968	291.847	226.995	45.396	-115.045	-78.055	5.825
800	112.968	306.931	236.065	56.693	-111.142	-73.041	4.769
860.000	112.968	315.101	241.298	63.471	II <--> LIQUID
900	112.968	320.237	244.693	67.990	107.664  68.493 3.975
1000	112.968	332.140	252.853	79.287	-104.917	-64.297	3.359
1100	112.968	342.907	260.558	90.583	-103.078	-60.310	2.864
1200	112.968	352.736	267.836	101.880	-100.704	-56.546	2.461
1300	112.968	361.778	274.719	113.177	-96.706	-53.029	2.131
1400	112.968	370.150	281.240	124.474	-92.823	-49.816	1.859
1500	112.968	377.944	287.430	135.771	-89.065	-46.876	1.632
1600	112.968	385.235	293.318	147.067	-85.440	-44.183	1.442
1700	112.968	392.084	298.928	158.364	-82.907	-41.693	1.281
1800	112.968	398.541	304.285	169.661	-79.907	-39.356	1.142
1900	112.968	404.649	309.408	180.958	-91.159	-36.479	1.003
2000	112.968	410.443	314.316	192.255	-88.705	-33.665	0.879