Lithium Iodide (LiI)	I1Li1(cr,l)
T(K)	Cp	S	-[G-H(Tr)]/T	H-H(Tr)	delta-f H	delta-f G	log Kf
0														
100														
200														
298.15	50.082	85.772	85.772	0.	-270.077	-269.665	47.244
300	50.187	86.082	85.773	0.093	-270.080	-269.662	46.952
400	53.430	100.875	87.767	5.243	-278.350	-269.208	35.155
500	55.948	113.073	91.645	10.714	-302.910	-264.545	27.637
600	58.660	123.499	96.104	16.437	-302.047	-256.948	22.369
700	62.258	132.807	100.693	22.480	-300.814	-249.523	18.620
742.000	63.764	136.478	102.615	25.126	CRYSTAL <--> LIQUID
742.000	63.178	156.214	102.615	39.770	TRANSITION
800	63.178	160.969	106.676	43.435	-284.644	-243.444	15.895
900	63.178	168.410	113.130	49.752	-283.113	-238.386	13.836
1000	63.178	175.067	118.997	56.070	-281.582	-233.498	12.197
1100	63.178	181.088	124.372	62.388	-280.053	-228.764	10.863
1200	63.178	186.586	129.331	68.706	-278.527	-224.169	9.758
1300	63.178	191.643	133.932	75.024	-277.010	-219.700	8.828
1400	63.178	196.325	138.224	81.342	-275.502	-215.348	8.035
1500	63.178	200.684	142.244	87.659	-274.005	-211.104	7.351
1600	63.178	204.761	146.025	93.977	-272.525	-206.959	6.757
1700	63.178	208.591	149.594	100.295	-416.302	-195.730	6.014
1800	63.178	212.202	152.973	106.613	-414.116	-182.818	5.305
1900	63.178	215.618	156.181	112.931	-411.965	-170.027	4.674
2000	63.178	218.859	159.234	119.249	-409.851	-157.349	4.110
2100	63.178	221.941	162.148	125.566	-407.773	-144.775	3.601
2200	63.178	224.880	164.933	131.884	-405.731	-132.299	3.141
2300	63.178	227.689	167.601	138.202	-403.721	-119.916	2.723
2400	63.178	230.378	170.161	144.520	-401.739	-107.619	2.342
2500	63.178	232.957	172.622	150.838	-399.782	-95.404	1.993