Magnesium Iodide (MgI2)	I2Mg1(l)
T(K)	Cp	S	-[G-H(Tr)]/T	H-H(Tr)	delta-f H	delta-f G	log Kf
0														
100														
200														
298.15	74.810	155.737	155.737	0.	-342.252	-344.316	60.323
300	74.977	156.200	155.738	0.139	-342.260	-344.329	59.953
400	78.408	178.261	158.723	7.815	-358.776	-344.389	44.973
500	80.919	196.035	164.464	15.785	-401.669	-336.671	35.172
600	83.011	210.980	171.004	23.985	-399.991	-323.827	28.192
600.000	83.011	210.980	171.004	23.985	GLASS <--> LIQUID
600.000	100.416	210.980	171.004	23.985	TRANSITION
700	100.416	226.459	177.849	34.027	-396.589	-311.403	23.237
800	100.416	239.867	184.782	44.068	-393.315	-299.459	19.553
900	100.416	251.695	191.572	54.110	-390.182	-287.917	16.710
907.000	100.416	252.473	192.040	54.813	CRYSTAL <--> LIQUID
1000	100.416	262.275	198.123	64.152	395.798  276.003 14.417
1100	100.416	271.845	204.397	74.193	-393.003	-264.159	12.544
1200	100.416	280.583	210.387	84.235	-390.225	-252.568	10.994
1300	100.416	288.620	216.100	94.276	-387.470	-241.209	9.692
1400	100.416	296.062	221.549	104.318	-512.156	-226.893	8.465
1500	100.416	302.990	226.750	114.360	-508.120	-206.658	7.196
1600	100.416	309.471	231.720	124.401	-504.134	-186.691	6.095
1700	100.416	315.558	236.474	134.443	-500.207	-166.972	5.130
1800	100.416	321.298	241.029	144.484	-496.345	-147.481	4.280
1900	100.416	326.727	245.398	154.526	-492.552	-128.204	3.525
2000	100.416	331.878	249.594	164.568	-488.830	-109.124	2.850