Zirconium Iodide (ZrI2)	I2Zr1(l)
T(K)	Cp	S	-[G-H(Tr)]/T	H-H(Tr)	delta-f H	delta-f G	log Kf
0														
100														
200														
298.15	94.140	186.168	186.168	0.	-234.239	-243.529	42.665
300	94.349	186.751	186.170	0.174	-234.212	-243.586	42.412
400	95.019	213.982	189.878	9.641	-248.943	-246.357	32.171
500	95.855	235.276	196.904	19.186	-290.220	-241.779	25.258
600	96.609	252.818	204.804	28.808	-287.043	-232.389	20.231
700	97.445	267.672	212.750	38.445	-283.939	-223.526	16.680
700.000	97.445	267.672	212.750	38.445	CRYSTAL <--> LIQUID
800	106.148	281.251	220.471	48.625	280.389  215.128 14.046
900	114.893	294.259	227.951	59.677	-276.075	-207.222	12.027
1000	123.595	306.815	235.213	71.602	-271.008	-199.836	10.438
1100	132.298	319.003	242.279	84.396	-265.200	-192.994	9.165
1200	141.001	330.887	249.170	98.061	-262.369	-186.492	8.118
1300	149.704	342.517	255.905	112.596	-254.559	-180.480	7.252
1400	158.448	353.931	262.500	128.004	-245.949	-175.099	6.533
1500	167.151	365.160	268.971	144.284	-236.560	-170.362	5.933
1600	175.854	376.225	275.329	161.434	-226.413	-166.275	5.428
1700	184.556	387.148	281.586	179.455	-215.529	-162.846	5.004
1800	193.259	397.943	287.751	198.345	-203.925	-160.078	4.645
1900	202.004	408.626	293.832	218.108	-191.613	-157.975	4.343
2000	210.706	419.209	299.837	238.744	-178.604	-156.538	4.088