Magnesium Silicide (Mg2Si)	Mg2Si1(cr)
T(K)	Cp	S	-[G-H(Tr)]/T	H-H(Tr)	delta-f H	delta-f G	log Kf
0														
100														
200														
298.15	67.864	81.588	81.588	0.	-77.822	-77.055	13.500
300	67.994	82.008	81.589	0.126	-77.826	-77.050	13.416
400	73.764	102.413	84.332	7.232	-77.951	-76.770	10.025
500	77.278	119.268	89.683	14.793	-78.002	-76.468	7.989
600	79.831	133.589	95.837	22.651	-78.054	-76.157	6.630
700	82.006	146.062	102.140	30.745	-78.152	-75.833	5.659
800	83.889	157.137	108.335	39.041	-78.342	-75.491	4.929
900	85.688	167.122	114.321	47.520	-78.661	-75.117	4.360
1000	87.404	176.239	120.064	56.175	-96.329	-73.274	3.827
1100	89.077	184.649	125.558	65.000	-97.022	-70.933	3.368
1200	90.667	192.468	130.812	73.987	-97.596	-68.536	2.983
1300	92.257	199.788	135.839	83.134	-98.052	-66.095	2.656
1375.000	93.450	204.996	139.470	90.098	CRYSTAL <--> LIQUID
1400	93.805	206.684	140.655	92.439	353.209  57.289 2.137
1500	95.312	213.207	145.277	101.896	-350.734	-36.237	1.262
1600	96.776	219.405	149.718	111.500	-348.152	-15.354	0.501
1700	98.198	225.315	153.992	121.249	-395.645	5.811	-0.179
1800	99.579	230.967	158.113	131.139	-392.633	29.339	-0.851
1900	100.918	236.387	162.091	141.164	-389.485	52.697	-1.449
2000	102.215	241.597	165.937	151.321	-386.205	75.886	-1.982
2100	103.470	246.615	169.660	161.606	-382.798	98.907	-2.460
2200	104.684	251.456	173.268	172.014	-379.268	121.763	-2.891
2300	105.855	256.136	176.770	182.541	-375.620	144.456	-3.281
2400	106.985	260.665	180.172	193.183	-371.859	166.988	-3.634
2500	108.073	265.054	183.480	203.936	-367.989	189.360	-3.956