Silicon Nitride, Alpha (Si3N4)	N4Si3(cr)
T(K)	Cp	S	-[G-H(Tr)]/T	H-H(Tr)	delta-f H	delta-f G	log Kf
0														
100														
200														
298.15	99.533	112.967	112.967	0.	-744.752	-647.343	113.412
300	99.788	113.583	112.969	0.184	-744.787	-646.739	112.607
400	110.667	143.790	117.014	10.711	-746.459	-613.792	80.153
500	120.708	169.582	125.007	22.288	-747.595	-580.482	60.643
600	129.704	192.417	134.374	34.826	-748.151	-546.998	47.620
700	138.072	213.048	144.162	48.220	-748.186	-513.462	38.315
800	145.812	232.003	153.973	62.424	-747.729	-479.956	31.338
900	152.298	249.566	163.631	77.342	-746.850	-446.533	25.916
1000	158.155	265.920	173.051	92.869	-745.635	-413.227	21.585
1100	163.678	281.258	182.198	108.966	-744.100	-380.058	18.047
1200	168.490	295.712	191.061	125.581	-742.280	-347.041	15.106
1300	172.531	309.362	199.641	142.637	-740.233	-314.187	12.624
1400	175.920	322.276	207.944	160.065	-738.019	-281.496	10.503
1500	178.657	334.510	215.977	177.799	-735.694	-248.968	8.670
1600	180.548	346.102	223.751	195.762	-733.327	-216.597	7.071
1700	182.171	357.098	231.274	213.900	-881.495	-183.033	5.624
1800	183.452	367.548	238.557	232.183	-878.469	-142.034	4.122
1900	184.539	377.496	245.610	250.584	-875.367	-101.205	2.782
2000	185.435	386.986	252.444	269.084	-872.202	-60.541	1.581
2100	185.780	396.041	259.068	287.645	-869.010	-20.037	0.498
2200	186.111	404.692	265.492	306.240	-865.814	20.316	-0.482
2300	186.429	412.972	271.725	324.867	-862.612	60.523	-1.375
2400	186.734	420.913	277.777	343.525	-859.403	100.590	-2.189
2500	187.025	428.541	283.656	362.213	-856.187	140.524	-2.936
2600	187.303	435.882	289.371	380.930	-852.962	180.329	-3.623
2700	187.567	442.956	294.929	399.673	-849.729	220.009	-4.256
2800	187.818	449.782	300.338	418.443	-846.487	259.570	-4.842
2900	188.056	456.377	305.606	437.236	-843.236	299.015	-5.386
3000	188.280	462.756	310.738	456.053	-839.977	338.347	-5.891