Nickel (Ni)	Ni1(cr)
T(K)	Cp	S	-[G-H(Tr)]/T	H-H(Tr)	delta-f H	delta-f G	log Kf
0	0.	0.	INFINITE	-4.786	0.	0.	0.
100	13.631	7.454	50.235	-4.278	0.	0.	0.
200	22.468	20.200	32.143	-2.389	0.	0.	0.
250	24.397	25.432	30.290	-1.215	0.	0.	0.
298.15	25.987	29.870	29.870	0.	0.	0.	0.
300	26.024	30.031	29.871	0.048	0.	0.	0.
350	27.294	34.139	30.192	1.381	0.	0.	0.
400	28.493	37.863	30.922	2.776	0.	0.	0.
450	29.623	41.281	31.886	4.228	0.	0.	0.
500	31.045	44.473	32.986	5.743	0.	0.	0.
600	34.853	50.440	35.404	9.022	0.	0.	0.
631.000	39.832	52.263	36.187	10.144	Cp LAMBDA MAXIMUM
631.000	39.832	52.263	36.187	10.144	TRANSITION
700	30.794	55.575	37.941	12.344	0.	0.	0.
800	31.003	59.697	40.408	15.431	0.	0.	0.
900	31.589	63.382	42.759	18.560	0.	0.	0.
1000	32.217	66.742	44.992	21.750	0.	0.	0.
1100	32.928	69.845	47.112	25.007	0.	0.	0.
1200	33.681	72.742	49.128	28.336	0.	0.	0.
1300	34.518	75.471	51.051	31.746	0.	0.	0.
1400	35.397	78.061	52.888	35.241	0.	0.	0.
1500	36.317	80.534	54.649	38.827	0.	0.	0.
1600	37.279	82.908	56.342	42.506	0.	0.	0.
1700	38.284	85.199	57.972	46.286	0.	0.	0.
1728.000	38.535	85.827	58.419	47.361	CRYSTAL <--> LIQUID
1800	39.330	87.411	59.547	50.156	17.161 0.715  0.021
1900	42.677	89.637	61.072	54.275	-16.933	1.704	-0.047
2000	43.806	91.855	62.556	58.599	-16.501	2.674	-0.070
2100	44.978	94.021	64.003	63.038	-15.953	3.620	-0.090
2200	46.191	96.141	65.415	67.596	-15.286	4.536	-0.108
2300	47.447	98.222	66.797	72.278	-14.495	5.420	-0.123
2400	48.702	100.268	68.149	77.085	-13.579	6.267	-0.136
2500	49.957	102.281	69.474	82.018	-12.537	7.073	-0.148