Nickel Sulfide (NiS2)	Ni1S2(cr,l)
T(K)	Cp	S	-[G-H(Tr)]/T	H-H(Tr)	delta-f H	delta-f G	log Kf
0														
100														
200														
250														
298.15	70.626	71.965	71.965	0.	-131.378	-124.813	21.867
300	70.664	72.402	71.966	0.131	-131.379	-124.772	21.725
400	72.739	93.015	74.763	7.301	-136.131	-122.358	15.978
500	74.814	109.469	80.112	14.678	-139.577	-118.542	12.384
600	76.889	123.292	86.186	22.264	-142.439	-114.057	9.930
700	78.965	135.301	92.363	30.056	-144.663	-109.134	8.144
800	81.040	145.981	98.410	38.057	-146.172	-103.951	6.787
900	83.115	155.646	104.241	46.264	-253.607	-96.438	5.597
1000	85.190	164.510	109.830	54.680	-252.093	-79.055	4.129
1100	87.266	172.727	115.179	63.302	-250.470	-61.829	2.936
1200	89.341	180.409	120.298	72.133	-248.744	-44.755	1.948
1280.000	91.001	186.228	124.238	79.346	CRYSTAL <--> LIQUID
1280.000	91.002	237.691	124.238	145.219	TRANSITION
1300	91.002	239.102	125.995	147.039	-181.052	-28.858	1.160
1400	91.002	245.846	134.318	156.140	-179.283	-17.218	0.642
1500	91.002	252.124	141.965	165.240	-177.635	-5.700	0.199
1600	91.002	257.998	149.035	174.340	-176.111	5.712	-0.186
1700	91.002	263.515	155.609	183.440	-174.715	17.032	-0.523
1800	91.002	268.716	161.749	192.540	-190.600	28.989	-0.841