Titanium Oxide, Beta (TiO)	O1Ti1(cr)
T(K)	Cp	S	-[G-H(Tr)]/T	H-H(Tr)	delta-f H	delta-f G	log Kf
0														
100														
200														
298.15	39.957	38.077	38.077	0.000	-538.481	-510.080	89.364
300	40.062	38.324	38.078	0.074	-538.480	-509.904	88.782
400	44.978	50.582	39.715	4.346	-538.307	-500.396	65.345
500	48.242	60.987	42.956	9.015	-537.908	-490.961	51.290
600	50.836	70.016	46.730	13.972	-537.356	-481.621	41.929
700	53.095	78.026	50.639	19.171	-536.673	-472.384	35.250
800	55.187	85.254	54.521	24.586	-535.851	-463.255	30.247
900	57.153	91.868	58.309	30.204	-534.927	-454.235	26.363
1000	59.078	97.990	61.974	36.016	-533.967	-445.321	23.261
1100	60.961	103.709	65.511	42.018	-533.035	-436.501	20.728
1200	62.802	109.093	68.921	48.206	-536.116	-427.646	18.615
1265.000	64.013	112.436	71.071	52.327	ALPHA <--> BETA
1300	64.643	114.192	72.209	54.578	534.515  418.671 16.822
1400	66.442	119.048	75.382	61.133	-532.827	-409.822	15.291
1500	68.241	123.694	78.449	67.867	-531.063	-401.098	13.967
1600	70.040	128.155	81.417	74.781	-529.238	-392.492	12.814
1700	71.839	132.456	84.294	81.875	-527.362	-384.003	11.799
1800	73.597	136.612	87.086	89.147	-525.452	-375.625	10.900
1900	75.396	140.639	89.799	96.597	-523.520	-367.354	10.099
2000	77.153	144.551	92.439	104.224	-536.265	-358.732	9.369
2023.000	77.551	145.436	93.037	106.003	BETA <--> LIQUID
2100	78.910	148.358	95.012	112.027	535.079  349.883 8.703
2200	80.668	152.069	97.521	120.006	-533.728	-341.095	8.099
2300	82.467	155.695	99.972	128.163	-532.210	-332.373	7.548
2400	84.224	159.242	102.368	136.497	-530.526	-323.720	7.046
2500	85.981	162.716	104.713	145.008	-528.677	-315.140	6.584