Silicon Sulfide (SiS2)	S2Si1(cr)
T(K)	Cp	S	-[G-H(Tr)]/T	H-H(Tr)	delta-f H	delta-f G	log Kf
0														
100														
200														
250														
298.15	77.488	80.333	80.333	0.	-213.384	-212.609	37.248
300	77.508	80.812	80.334	0.143	-213.362	-212.605	37.018
400	78.617	103.260	83.387	7.949	-216.872	-212.329	27.727
500	79.789	120.915	89.189	15.863	-219.092	-210.962	22.039
600	81.714	135.657	95.737	23.952	-220.548	-209.185	18.211
700	82.006	148.265	102.363	32.131	-221.511	-207.211	15.462
800	83.136	159.289	108.804	40.388	-222.185	-205.119	13.393
900	84.266	169.146	114.970	48.758	-328.891	-200.795	11.654
1000	85.395	178.083	120.842	57.241	-326.731	-186.677	9.751
1100	86.525	186.275	126.423	65.837	-324.534	-172.778	8.205
1200	87.655	193.852	131.730	74.546	-322.297	-159.081	6.925
1300	88.784	200.913	136.783	83.368	-320.021	-145.571	5.849
1363.000	89.496	205.131	139.846	88.984	CRYSTAL <--> LIQUID
1400	89.915	207.534	141.603	92.303	317.704  132.239 4.934
1500	91.044	213.776	146.208	101.351	-315.347	-119.073	4.146
1600	92.154	219.687	150.618	110.511	-312.950	-106.066	3.463
1700	93.270	225.307	154.847	119.782	-360.689	-92.764	2.850
1800	94.391	230.670	158.912	129.165	-357.979	-77.081	2.237
1900	95.518	235.804	162.824	138.660	-355.182	-61.552	1.692
2000	96.650	240.732	166.597	148.269	-352.296	-46.172	1.206