Silicon Sulfide (SiS2)	S2Si1(l)
T(K)	Cp	S	-[G-H(Tr)]/T	H-H(Tr)	delta-f H	delta-f G	log Kf
0														
100														
200														
250														
298.15	77.488	84.687	84.687	0.	-206.924	-207.448	36.344
300	77.508	85.166	84.688	0.143	-206.902	-207.451	36.120
400	78.617	107.614	87.742	7.949	-210.412	-207.610	27.111
500	79.789	125.269	93.543	15.863	-212.632	-206.679	21.592
600	81.714	140.011	100.091	23.952	-214.089	-205.337	17.876
700	82.006	152.619	106.717	32.131	-215.051	-203.799	15.208
800	83.136	163.643	113.158	40.388	-215.725	-202.142	13.199
900	84.266	173.500	119.324	48.758	-322.431	-198.254	11.506
900.000	84.266	173.500	119.324	48.758	GLASS <--> LIQUID
900.000	91.002	173.500	119.324	48.758	TRANSITION
1000	91.002	183.088	125.230	57.858	-319.654	-184.606	9.643
1100	91.002	191.762	130.890	66.958	-316.952	-171.232	8.131
1200	91.002	199.680	136.297	76.059	-314.325	-158.102	6.882
1300	91.002	206.964	141.457	85.159	-311.770	-145.187	5.834
1363.000	91.002	211.270	144.585	90.892	CRYSTAL <--> LIQUID
1400	91.002	213.708	146.380	94.259	309.288  132.467 4.942
1500	91.002	219.986	151.080	103.359	-306.879	-119.921	4.176
1600	91.002	225.859	155.572	112.459	-304.541	-107.534	3.511
1700	91.002	231.376	159.871	121.560	-352.452	-94.844	2.914
1800	91.002	236.578	163.989	130.660	-350.024	-79.760	2.315
1900	91.002	241.498	167.940	139.760	-347.622	-64.811	1.782
2000	91.002	246.166	171.736	148.860	-345.244	-49.988	1.306