Silicon Sulfide (SiS2)	S2Si1(cr,l)
T(K)	Cp	S	-[G-H(Tr)]/T	H-H(Tr)	delta-f H	delta-f G	log Kf
0														
100														
200														
250														
298.15	77.488	80.333	80.333	0.	-213.384	-212.609	37.248
300	77.508	80.812	80.334	0.143	-213.362	-212.605	37.018
400	78.617	103.260	83.387	7.949	-216.872	-212.329	27.727
500	79.789	120.915	89.189	15.863	-219.092	-210.962	22.039
600	81.714	135.657	95.737	23.952	-220.548	-209.185	18.211
700	82.006	148.265	102.363	32.131	-221.511	-207.211	15.462
800	83.136	159.289	108.804	40.388	-222.185	-205.119	13.393
900	84.266	169.146	114.970	48.758	-328.891	-200.795	11.654
1000	85.395	178.083	120.842	57.241	-326.731	-186.677	9.751
1100	86.525	186.275	126.423	65.837	-324.534	-172.778	8.205
1200	87.655	193.852	131.730	74.546	-322.297	-159.081	6.925
1300	88.784	200.913	136.783	83.368	-320.021	-145.571	5.849
1363.000	89.496	205.131	139.846	88.984	CRYSTAL <--> LIQUID
1363.000	91.002	211.270	139.846	97.352	TRANSITION
1400	91.002	213.708	141.766	100.719	-309.288	-132.467	4.942
1500	91.002	219.986	146.773	109.819	-306.879	-119.921	4.176
1600	91.002	225.859	151.535	118.919	-304.541	-107.534	3.511
1700	91.002	231.376	156.071	128.020	-352.452	-94.844	2.914
1800	91.002	236.578	160.400	137.120	-350.024	-79.761	2.315
1900	91.002	241.498	164.540	146.220	-347.622	-64.811	1.782
2000	91.002	246.166	168.506	155.320	-345.244	-49.988	1.306