Zirconium, Beta (Zr)	Zr1(cr)
T(K)	Cp	S	-[G-H(Tr)]/T	H-H(Tr)	delta-f H	delta-f G	log Kf
0														
100														
200														
250														
298.15	25.202	43.192	43.192	0.	4.810	3.521	-0.617
300	25.218	43.348	43.193	0.047	4.810	3.513	-0.612
350	25.587	47.264	43.501	1.317	4.809	3.297	-0.492
400	25.935	50.703	44.191	2.605	4.809	3.081	-0.402
450	26.238	53.775	45.088	3.909	4.808	2.865	-0.333
500	26.564	56.557	46.098	5.229	4.808	2.649	-0.277
600	27.281	61.462	48.261	7.921	4.809	2.217	-0.193
700	28.053	65.724	50.457	10.687	4.808	1.785	-0.133
800	28.966	69.535	52.608	13.542	4.813	1.353	-0.088
900	28.473	72.916	54.681	16.412	4.736	0.923	-0.054
1000	28.238	75.902	56.656	19.245	4.513	0.511	-0.027
1100	28.260	78.592	58.530	22.068	4.164	0.126	-0.006
1135.000	28.329	79.478	59.163	23.058	ALPHA <--> BETA
1200	28.511	81.060	60.306	24.905	0. 0. 0.
1300	28.879	83.356	61.992	27.774	0.	0.	0.
1400	29.353	85.513	63.596	30.684	0.	0.	0.
1500	29.934	87.558	65.126	33.648	0.	0.	0.
1600	30.621	89.511	66.589	36.675	0.	0.	0.
1700	31.414	91.390	67.993	39.776	0.	0.	0.
1800	32.314	93.211	69.344	42.961	0.	0.	0.
1900	33.320	94.985	70.647	46.242	0.	0.	0.
2000	34.433	96.722	71.907	49.629	0.	0.	0.
2100	35.652	98.431	73.130	53.132	0.	0.	0.
2125.000	35.973	98.854	73.430	54.027	BETA <--> LIQUID
2200	36.977	100.119	74.318	56.763	21.323 0.746  0.018
2300	38.409	101.794	75.476	60.531	-21.738	1.759	-0.040
2400	39.947	103.461	76.608	64.448	-22.005	2.786	-0.061
2500	41.591	105.125	77.715	68.524	-22.113	3.822	-0.080
2600	43.342	106.790	78.801	72.770	-22.052	4.859	-0.098